Ki diferans ki genyen ant yon jete-nan zepòl ak yon soude-sou zepòl?

LaRail zepòlse yon pati semi-- entegre ki jete nan lyen ray konkrè yo pou ranje clip tren elastik la sou plak baz la, Gen de kalite epòl ray komen ki disponib nan GNEE RAIL,Jete-nan zepòlepiSoude-sou zepòl, tou de yo itilize pou fikse klip tren elastik. Youn se Single Stem Iron Shoulder yo itilize nan lyen konkrè pre-ensiste ak lòt la se Twin Stem Iron Shoulder yo itilize nan Bi-Blòk oswa Twin Block lyen konkrè.

 

Epòl ray Customized pou vann

 

• Materyèl:QT400-15,QT450-10,QT500-7,QT600-3,QT700-2,ZG25,ZG35,ZG45

 

• Modèl: Customized selon desen an

 

• Sifas: Plain-lwilize, oksijèn nwa

 

• Kalite pwodwi: Distribisyon sab, fòje cho

 

 

 

Diferans prensipal la se metòd enstalasyon yo: ajete-nan zepòlse pre-anke nan yon travès konkrè pandan fabrikasyon li, pandan y ap asoude-sou zepòlse yon eleman ki soude sou yon plak baz asye oswa yon travès asye. Jete-nan zepòl yo se pou aplikasyon estanda mare konkrè, tandiske soude-sou zepòl yo itilize pou travès asye oswa sitiyasyon kote enstalasyon estanda pa posib.

 

 

Karakteristik	Jete-nan zepòl	Soude-sou zepòl
Enstalasyon	Pre-anke nan yon travès konkrè	Soude sou yon plak baz asye oswa yon travès asye
Aplikasyon Prensipal	Travès estanda konkrè	Travès asye ak plak baz kote travès estanda pa ka itilize
Pwosesis Faktori	Fè jete	Cho fòje
Fleksibilite	Mwens fleksib, kòm li se yon pati pèmanan nan travès la konkrè	Plis fleksib, kòm li ka soude sou pou ajisteman oswa satisfè bezwen espesifik konsepsyon
Sèvi ak ka	Itilize nan ray tren estanda	Itilize nan layout espesyal, switch, travèse, oswa pou reparasyon / chanjman

 

 

 

Aplikasyon	UIC54	UIC60	115RE, 50kg tren, 60kg tren, BS80lbs, BS100lbs, ect.
Non	QT500-7	QT450-10	QT400-15
Estanda	GB 1348-88	GB 1348-88	GB 1348-89
Konpozisyon chimik (%)	C:3.60-3.80	C:3.40-3.90	C:3.50-3.60
	C:3.60-3.80	Mn:0.2-0.5	Mn: Mwens pase oswa egal a 0.5
	Si:2.50-2.90	Si:2.70-3.00	Si:3.0-3.2
	P: Mwens pase oswa egal a 0.08	P: Mwens pase oswa egal a 0.07	P: Mwens pase oswa egal a 0.07
	S: Mwens pase oswa egal a 0.025	S: Mwens pase oswa egal a 0.03	S: Mwens pase oswa egal a 0.02
Fòs rupture	Pi gran pase oswa egal a 500 Mpa	Pi gran pase oswa egal a 450 Mpa	Pi gran pase oswa egal a 400 Mpa
Sede fòs	Pi gran pase oswa egal a 320 Mpa	Pi gran pase oswa egal a 310 Mpa	Pi gran pase oswa egal a 250 Mpa
elongasyon (%)	Pi gran pase oswa egal a 7	Pi gran pase oswa egal a 10	Pi gran pase oswa egal a 15
Dite	170 ~ 230HB	160 ~ 210HB	130 ~ 180HB
Òganizasyon metalografik	ferit ak pèrlit	grafit & ferit & pearlite	ferit

 

Jete-nan pwopriyete mekanik zepòl ray

 

Materyèl	QT500-7	QT450-10	QT400-15
Fòs rupture	Pi gran pase oswa egal a 500 Mpa	Pi gran pase oswa egal a 450 Mpa	Pi gran pase oswa egal a 400 Mpa
Sede fòs	Pi gran pase oswa egal a 320 Mpa	Pi gran pase oswa egal a 310 Mpa	Pi gran pase oswa egal a 250 Mpa
Elongasyon	Pi gran pase oswa egal a 7	Pi gran pase oswa egal a 10	Pi gran pase oswa egal a 15
Dite	170 ~ 230HB	160 ~ 210HB	130 ~ 180HB

 

Jete-nan Rail Zepòl Konpozisyon Chimik Kondisyon

 

Materyèl	C	Si	Mn	P	S
QT400-15	3.6-.36	3.0-3.2	0.5	0.07	0.02
Qt450-10	3.4-3.9	3.7-3.0	0.5	0.07	0.03
QT500-7	3.4-3.8	2.5-2.9	0.6	0.08	0.025

 